Filaments
Sharebot 3D printing filament are available in a wide range of colors and materials and are the perfect solution for professionals who are looking for high quality and technical features for their 3D printing process.
Sharebot 3D printing filament are available in a wide range of colors and materials and are the perfect solution for professionals who are looking for high quality and technical features for their 3D printing process.
PLA’s the most used 3D printing material, composed by a thermoplastic polymer derivated from corn and it’s biodegradable. PLA’s resistant and solid (avoiding the warping effect during the printing process) without retraction and deformation. Available in a lot of different colors, it doesn’t release any smell and it can be extruded at lower temperatures than any other material without having to heat the printing bed.
PROPERTY | VALUE | TEST |
---|---|---|
MELTING POINT | 140° -160°C | D3418 |
TENSILE MODULUS | MD 480 KPSI TD 560 KPSI | D882 D882 |
TENSILE STRENGTH | MD 16 KPSI TD 21 KPSI | D882 D882 |
DEGRADATION | 250°C | |
T° EXTRUSION | 215°C | |
T° PLATE | 30° – 60°C (NOT REQUIRED) |
ABSolute® is a new generation ABS filament developed to give the best functioning material to the professional user. During the printing process there is no warpring effect and no retraction of the filament on the printing plate, avoiding any failure of your process. ABSolute® is the perfect materia for professionals looking for high impact resistance and high temperature.
PROPERTY | VALUE | TEST |
---|---|---|
MELTING POINT | 230°C | ISO 294 |
TENSILE MODULUS | 2030 MPA | ISO 527 |
TENSILE STRENGTH | 43,6 MPA | ISO 527 |
DEGRADATION | ||
T° EXTRUSION | 240° – 260° | |
T° PLATE | 80° – 90°C |
It is an elastic polymeric material that could be stretched and forced without damaging it: TPU will always come back to its original form. The filament is available in a lot of different colors and during the printing process it doesn’t give off any smell. You can find on our website a tutorial in order to learn how to print it.
PROPERTY | VALUE | TEST |
---|---|---|
MELTING POINT | 225° – 245°C | |
TENSILE MODULUS | 150 MPA | ISO 527 1/2 |
TENSILE STRENGTH | 50 MPA | ISO 527 1/2 |
DEGRADATION | ||
T° EXTRUSION | 225° – 250° | |
T° PLATE | MAX 90°C (NOT REQUIRED) |
Sharebot WOOD 3D printing filament is a mixture of modified PLA charged with true micronized wood powder. WOOD is printed at low temperatures and it can be easily carved with sand papers or tumbling machines after the printing process. Its porous texture allows to print it without using any primer so that the print can adhere on it.
PROPERTY | VALUE | TEST |
---|---|---|
MELTING POINT | 130° – 155°C | 03418 |
TENSILE MODULUS | 68 MPA | D790 |
TENSILE STRENGTH | 37 MPA | D638 |
DEGRADATION | 250°C | |
T° EXTRUSION | 200° | |
T° PLATE | 30 – 50°C |
Nylon-Glass is a material composed by a mix of nylon and glass fibers. The material allows to print precisie models with an excelent surface definition. It can be used in place of the common ABS thanks to its high resistance: our testers used it to realize mechanical functioning spare parts and prototypes. Because of its elastic components, the Nylon-Glass is very flexible and it can be bended without reaching the breaking point.
PROPERTY | VALUE | TEST |
---|---|---|
MELTING POINT | 180°C | 11357 |
TENSILE MODULUS | 4000 MPA | ISO 527 |
TENSILE STRENGTH | 95 MPA | ISO 527 |
DEGRADATION | 160°C | ISO 75 |
T° EXTRUSION | 240° | |
T° PLATE | 20°C |
Nylon-Carbon is a high quality material. It’s composed by 2 different fibres: nylon and carbon. Nylon gives to the filament a high resistance while carbon gives lightness, making it very easy to print. The printed object are resistant, with opaque black color, slightly rough and with a light metallic look. Nylon-Carbon is ideal for manufacturing use.
PROPERTY | VALUE | TEST |
---|---|---|
MELTING POINT | 180°C | 11357 |
TENSILE MODULUS | 6000 MPA | ISO 527 1/2 |
TENSILE STRENGTH | 100 MPA | ISO 527 1/2 |
DEGRADATION | 155°C | ISO 75 |
T° EXTRUSION | 240° | |
T° PLATE | 20°C (NOT REQUIRED) |
PPis our easy to print general purpose low density Polypropylene. PP has been developed for optical clarity while maintaining mechanical performance and a superb layer adhesion. PP high stretch ability, decent flexibility and chemical/fatigue resistance makes it suitable for a variety of household articles and containers. PP can also be used for engineering articles such as living-hinges and snap-fit fastener materials. It’s a cost-effective all round filament suitable for a broad variety of needs.
PROPERTY | VALUE | TEST |
---|---|---|
MELTING POINT | 190°C – 220°C | – |
TENSILE MODULUS | 402 MPA | D790 |
TENSILE STRENGTH | 12 MPA | D638 |
DEGRADATION | ±103°C | |
T° EXTRUSION | 230°C – 250°C | |
T° PLATE |
PET (polyethylene terephthalate), is a filament for industrial use with different exceptional characteristics.
It combines the ease of use of the PLA filament with the resistance and durability of the ABS filament. Firstly, its hardness is much higher than the PLA and is approved by the FDA for food containers and tools used for food consumption. Unlike the ABS filament, it does not produce odors or fumes when printed. The PET filament is not biodegradable, but is 100% recoverable.
PROPERTY | VALUE | TEST |
---|---|---|
HEAT DISTORTION TEMP. | 72°C | D648 |
FLEX. MODULUS | 2030 MPA | D790 |
TENSILE STRENGTH | 50 MPA | D638 |
GLASS TRANSITION TEMP. | ±62°C | D2418 |
T° EXTRUSION | 230°C – 240°C | |
T° PLATE | 75°C |